AKROMID® B3 GF 50 S1 black 950089 (2000)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qHvRPc_AKROMID-B3-GF-50-S1-black-950089-2000-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 50 S1 black 950089 (2000) is a 50% glass fibre reinforced, cold impact strength polyamide 6 with very high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.54 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 34.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.50 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.3 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15000 | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 190 | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | 8.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 20 | kJ/m² | |
| 23°C | 25 | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | > 100 | -- | kJ/m² | |
| 23°C | > 100 | > 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-CO-HF-30T | Pro Polymers | PP Copolymer | Pro-Comp™ |
| NuSil MED-4840 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| Fainplast PVC KL 0209 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KumhoSunny PMMA/ABS HAM8541 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Acrylic | KumhoSunny PMMA/ABS |
| Karina PVC COMPOUND WHITE COLOR - E-800-10/1-A-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |