AKROMID® A3 GM 15/15 black (1073)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q5C3kQ_AKROMID-A3-GM-15-15-black-1073-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GM 15/15 black (1073) is a 15% glass fibre reinforced, 15% glass bead filled polyamide 6.6 with good surface and low warpage. Applications are mainly components in mechanical enginneering and automotive industry with high surface requirements |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Saturation, 23°C) | 5.6 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.4 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7600 | 4600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7500 | 6200 | MPa | ISO 178 |
| Flexural Stress 2 | 220 | 155 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 41 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 263 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 244 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOFORCE® PEEK C2301 | LEIS Polytechnik - polymere Werkstoffe GmbH | PEEK | TRIBOFORCE® |
| APEX® 4111 | Teknor Apex Company | PVC, Flexible | APEX® |
| Etinox® 630P | Ercros, S.A. | PVC Homopolymer | Etinox® |
| DJSilicone NE-9170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| KOPA® KN333G35CR | Kolon Plastics, Inc. | Nylon 66 | KOPA® |