| 55NT is an epoxy laminate and prepreg system, reinforced with a non-woven aramid substrate. This system combines compatibility with lead-free processing, using a hightemperature epoxy resin, with the low in-plane (x,y) expansion and outstanding dimensional stability of non-woven aramid reinforcement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792A |
| Water Absorption (24 hr) | 0.30 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 368 | °C | |
| Initial | 351 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 1 | 630.5 | N/m | |
| -- 2 | 630.5 | N/m | |
| -- 3 | 630.5 | N/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 4 | 3.5 | % | Internal Method |
| T260 | > 1.0 | hr | Internal Method |
| T288 | > 1.0 | hr | Internal Method |
| T300 | 28.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | Internal Method |
| Tensile Strength | 248 | MPa | Internal Method |
| Flexural Strength | 262 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 170 | °C | Internal Method |
| CLTE - Flow | |||
| -- 5 | 6.0E-6 to 9.0E-6 | cm/cm/°C | Internal Method |
| < 160°C 6 | 9.9E-5 | cm/cm/°C | Internal Method |
| > 160°C 7 | 2.6E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.20 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 8 | 1.8E+14 | ohms | |
| -- 9 | 1.6E+15 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 10 | 2.3E+13 | ohms·cm | |
| -- 11 | 6.6E+13 | ohms·cm | |
| Dielectric Strength | 49 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 3.80 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.015 | Internal Method | |
| Arc Resistance | 165 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Process Solutions |
| 2 . | At Elevated Temperatures |
| 3 . | After Thermal Stress |
| 4 . | Z-axis |
| 5 . | Y-axis |
| 6 . | Z-axis |
| 7 . | Z-axis |
| 8 . | C96/35/90 |
| 9 . | E24/125 |
| 10 . | C96/35/90 |
| 11 . | E24/125 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA250FR | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Dryflex® 500650S | ELASTO | SEBS | Dryflex® |
| EL-Pro™ P602F | SCG Chemicals Co., Ltd. | PP Homopolymer | EL-Pro™ |
| MAXATEL® AH800AVL-NAT | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |
| Sylvin 8200-95UV Red 6259 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |