ShinkoLite-P UT-300
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | ShinkoLite-P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | psaNDL_ShinkoLite-P-UT-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ShinkoLite-P UT-300 is a Polymethyl Methacrylate Acrylic material. It is available in North America for extrusion or injection molding. Important attributes of ShinkoLite-P UT-300 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 3.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.8 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 74.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.8 | % | ASTM D638 |
| Flexural Modulus | 3240 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 0.30 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 78.3 to 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 1881 | Covestro - Polycarbonates | PC | Makrolon® |
| tefabloc® TO 132 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Sinvicomp SRP8625 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sindustris PC NS5001C | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| ALAMID® 6 HZ 4 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |