Clearflex® H&T CHH 196
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pn0Ox5_ClearflexHampTCHH196.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T CHH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films manufactured with Clearflex H&T CHH 196 have outstanding fracture mechanical properties, mainly Elmendorf tear strength along machine direction (MD) and puncture resistance. Moreover, the holding force is the key property of these films when used in automatic wrapping machines. Main Applications Clearflex H&T CHH 196 is recommended for production of super-power stretch films. Its properties, especially in terms of holding force and puncture resistance, make Clearflex H&T CHH 196 the ideal choice for packaging goods of irregular shape and for applications requiring a superior mechanical strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : 23 µm, cast film | 145 | MPa | ISO 527-3 |
| 1% sectioning, TD : 23 µm, cast film | 140 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 23 µm, cast film | 8.00 | MPa | ISO 527-3 |
| TD : yield, 23 µm, cast film | 9.00 | MPa | ISO 527-3 |
| MD : fracture, 23 µm, casting film | 40.0 | MPa | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 32.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : fracture, 23 µm, casting film | 600 | % | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 800 | % | ISO 527-3 |
| Dart Drop Impact (23 µm, Cast Film) | 330 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 23.0 µm | 130.0 | kN/m | ISO 6383-2 |
| TD : 23.0 µm | 240.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 92 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 2.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 270 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STERLENE™ RP0100230U | R&P (Pte.) Ltd. | PP, Unspecified | STERLENE™ |
| Karina IVORY PVC COMPOUND 900-35/ 1-AYR-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® ABS GFABS-10 | The Plastics Group | ABS | Polifil® ABS |
| SABIC® LDPE 2005EC | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Durethan® BKV 60 H2.0 EF DUS060 900116 | LANXESS GmbH | Nylon 6 | Durethan® |