POLYshine PBT D201
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYshine |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | olwQ8D_POLYshine-PBT-D201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYshine PBT D201 is a Polybutylene Terephthalate (PBT) product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 to 2.0 | % | |
| Flow | 1.8 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 178 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® C50 | Nilit Plastics | Nylon 66/6 | POLYNIL® |
| Anjacom® 10/25S-UV | Almaak International GmbH | PC+ABS | Anjacom® |
| Ferro PP TPP20AN50WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| EPO-TEK® 377 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Durethan® BKV 25 H2.0 LT 904040 | LANXESS GmbH | Nylon 6 | Durethan® |