Starex WX-9300UV
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oCMBvZ_Starex-WX-9300UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex WX-9300UV is an Acrylonitrile Styrene Acrylate (ASA) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.37 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.40 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.43 | % | ISO 2577 |
| Flow : 3.20 mm | 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 104 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 43.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break | 39.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 12 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2000 | MPa | ASTM D790 |
| -- 4 | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 62.0 | MPa | ASTM D790 |
| -- 6 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed, 4.00 mm) | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/B50 |
| -- | 99.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 TFE 15 FR L | RTP Company | PC | RTP |
| STERLENE™ BMU148A | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| 3M™ Dyneon™ Fluoroplastic PFA 6505TZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| BJB Polyurethane TC-896 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| COPYLENE® CR350CS-01 | Phillips 66 | PP Random Copolymer | COPYLENE® |