CALIBRE™ 1602 LTD
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nMm74P_CALIBRE-1602-LTD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 1602 LTD Polycarbonate Resin is designed to have good low temperature impact resistance compared to standard polycarbonate. The material has improved impact performance after heat aging relative to standard polycarbonate. The polymer features a good balance of mechanical properties. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1930 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 56.9 | MPa | ASTM D638 |
| Flexural Modulus | 2050 | MPa | ASTM D790 |
| Flexural Strength | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 480 | J/m | |
| 23°C | 540 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 136 | °C | |
| 1.8 MPa, Unannealed | 122 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 403 HI | RTP Company | PS (HIPS) | RTP |
| Ravago Compounds HM-307 (Comp) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| Rhelon X2000-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| WanBlend® WHT-HF8675 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Hipolyene 6251 Y | Zylog Plastalloys | TPO (POE) | Hipolyene |