Order Products : sales@su-jiao.com
Pibiter® HI C3311 NERO900
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiter® HI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iNQnwy_Pibiter-HI-C3311-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/PC alloy, high impact properties, medium fluidity |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.80 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 50.0 | MPa | |
| Break | 46.0 | MPa | |
| Tensile Elongation (Break) | 170 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 600 | J/m | |
| 23°C | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 245 | °C | |
| Middle Temperature | 255 | °C | |
| Front Temperature | 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 25 RS 4 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Sup-tech B801 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Amilan® CM1011G-15 | Toray Resin Company | Nylon 6 | Amilan® |
| Elastron® V P.V101.A55.B | Elastron USA, Inc. | TPV | Elastron® V |
| Hifax X M1 T11 356525 | LyondellBasell Industries | PP Copolymer | Hifax |