SABIC® LDPE HP2027N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nKnH0r_SABIC-LDPE-HP2027N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABIC® LDPE HP2027N is a Low Density Polyethylene grade without slip and anti-block additives, with increased density. It typically exhibits better draw down ability with high output. Films typically exhibit excellent optics and good heat seal properties combined with high rigidity. TYPICAL APPLICATIONS: Bags & pouches, surface protection films, lamination films, food packaging films. Films where high optics, enhanced stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 300 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction | > 80 | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 20 - 60 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 70 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 110 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 6.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Measured on 50 micron thickness blown film extruded at melt temperature of 180°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yanshan PE 1C5A | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| NEFTEKHIM PE 6948C (486H3) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Arlon® 1287 LI | Greene, Tweed & Co. | PEEK | Arlon® |
| Fainplast PVC PK 71/FR | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| SQUARE® LIM1939-60A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |