| DESCRIPTION: Epocast 927-1 GB epoxy syntactic is a frozen, one-component, structural material for reinforcing honeycomb parts that maintains high compressive strength at high temperatures. When thawed, the epoxy syntactic can be extruded from cartridges as a thixotropic paste. Epocast® 927-1 GB is qualified to RMS 027, type XV. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ASTM D1622 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 25°C 1 | 103 | MPa | ASTM D695 |
| 177°C 2 | 89.6 | MPa | ASTM D695 |
| 25°C | 124 | MPa | ASTM D695 |
| 177°C | 75.8 | MPa | ASTM D695 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Extrudability (25°C) | > 1000 | g/min | |
| Work Life - after thaw (25°C) | 1.0 | day | ASTM D1338 |
| Recommended cure cycle: Heat the material from room temperature at the rate of 3-4°C per minute, plus 1 hour at 177°C or 90 minutes at 121°C. Cure temperature refers to temperature of material determined by thermocouple. (Slow heat rise to 3-4°C preferred to reduce shrinkage and minimize out-gassing during cure). |
| Note Message | |
|---|---|
| 1 . | After 500 hours at 177°C |
| 2 . | After 500 hours at 177°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP QR678K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| GETILAN ATP/130 XPE | Crosspolimeri S.p.A. | XLPE | GETILAN |
| Kotex K-20UVR | Kotec Corporation | PC | Kotex |
| POLYfill PPH BF4075 VT1 | Polykemi AB | PP Homopolymer | POLYfill |
| MAXAMID™ RC6G33HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |