RapidCast™ RC-555
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidCast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nFLtGM_RapidCast-RC-555.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC 555 is a shore D polyurethane formulated for room temperature meter mix dispensing systems and short mold cycle times. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.10 | g/cm³ | |
| Cured | 1.14 | g/cm³ | |
| Base Resin | 1.26 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1280 | MPa | ASTM D790 |
| Flexural Strength | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 88 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 15 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.50 | Pa·s | |
| 25°C 3 | 1.2 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 1.0 to 1.3 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ASTM D2240 | |
| Tensile Strength | 32.4 | MPa | ASTM D638 |
| Tensile Elongation at Break | 9.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® SA-2105 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| SUPREME HIPS SH2157 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Toyolac® 250 X10 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| ICORENE® N9306 | ICO Polymers EMEA, A Division of A. Schulman | Acetal (POM) Copolymer | ICORENE® |
| Durez® 33824 | SBHPP | Phenolic | Durez® |