OmniTech™ POM 27
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oky0f7_OmniTech-POM-27.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy Flow, Injection Grade, Polyoxymethylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.5 to 2.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | < 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 191 to 210 | °C | |
| Middle Temperature | 191 to 210 | °C | |
| Front Temperature | 191 to 210 | °C | |
| Nozzle Temperature | 191 to 210 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 93.3 to 121 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProvaMed® PVC 3264 | ACTEGA GmbH | PVC, Unspecified | ProvaMed® PVC |
| PRL PC-FD2-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| TRANSMARE® 12CT20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Karina WHITE PVC COMPOUND 902-10/21-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| CYCOLOY™ XCY630 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |