BESTNYL SE35VI01AH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n4O3wT_BESTNYL-SE35VI01AH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural with 35% glass fibre reinforcement and heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Ash Content | 35 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12800 | MPa | ISO 527-2 |
| Tensile Stress | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | > 260 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 34 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 275 to 290 | °C | |
| Mold Temperature | 90.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7CSN (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Next Nylon 6 Prime Series NG40-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Borealis PP MB350WG | Borealis AG | PP, Unspecified | Borealis PP |
| Petrothene® GA501150X01 | LyondellBasell Industries | LLDPE | Petrothene® |
| Rotuba CAB B9086 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |