| VITAMIDE® BG35NT6747 is a Polyamide 6 (Nylon 6) product filled with 25% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 1.7 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 87.5 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 7.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 30.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 21 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- 3 | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 33 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PH035L | Premier Polymers, LLC. | PP Homopolymer | Premier |
| Shandong PA610 Type III | Shandong Guangyin New Materials Co., Ltd. | Nylon 610 | Shandong PA610 |
| Cosmic Epoxy E4920D | Cosmic Plastics, Inc. | Epoxy | Cosmic Epoxy |
| Elastollan® S 95 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Plexiglas® V825-UVA5A | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |