Nirion F10 V0
| Category: | PC , Polycarbonate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Nirion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mvsetw_Nirion-F10-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate reinforced with 10% glass fibre, flame retardant as per UL 94 V0 at 1.6 mm rating. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 3200 | MPa | ASTM D790 |
| Flexural Strength 2(Break) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 147 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 82109 | RTP Company | PEI | RTP |
| REXtac® APAO RT 2830 | Huntsman Corporation | PAO | REXtac® APAO |
| Crastin® S620F20 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| KOPA® KN333HI5Bl1 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Sylvin 4215-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |