Ixef® 2030
| Category: | PARA , Polyarylamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ixef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mggSEG_Ixef-2030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ixef 2030 is a 55% glass fiber/mineral reinforced polyaramide compound with high strength, excellent rigidity, low warpage, excellent creep resistance and excellent surface gloss. -Black: Ixef 2030/X927 -Customers can color by themselves |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.10 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.19 | % | ISO 62 |
| Water absorption- Equil, 65% RH | 1.6 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Flexural Modulus | 19000 | MPa | ISO 178 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/A |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant (110 Hz) | 4.80 | IEC 60250 | |
| Dissipation Factor (110 Hz) | 0.025 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | HB | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 0.50 - 1.5 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Injection instructions |
|---|
| 热流道系统：250 °C～260 °C （ 482°F～500 °F ） 射出压力：快速 G3185 干燥：所提供的成型用材料无需干燥处理。但是，如果袋已被打开超过24小时，必须先干燥材料。如果使用的 除湿空气干燥机露点为-28 ° C（ -18 °F ）或更低，应遵循以下规则：120 ° C（248 °F）温度下 0.5〜1.5小时， 100℃ C（ 212°F）温度下1〜3个小时，或80 ℃（176 °F）温度下1-7个小时。 注塑成型： IXEF 2030混合物在大多数螺杆注塑机上均可以很容易地注射成型。建议采用通用螺杆，取最小背压。 测得的熔融温度应该在280℃ （536° F）左右，机筒后端温度应该在250～260℃ （ 482～500°F ）左右，前端逐渐增至260 ℃〜290℃ （500～554 °F）。如果使用热流道，温度应设置为250～260 ℃（482～500 ° F ） 。 为了最大限度地提高结晶度，模腔表面温度必须保持在120～140℃（ 248～284°F）之间。成型温度低，容易使产品产生翘曲、外观不良，并极可能产生蠕变。射出压力应确保快速射出。调整保压压力和时间，尽量提高零件的重量。部件正好完全填充完毕（ 95-99％）前，将注塑件从射出部位转移到螺杆位置进行保压。 |
| Note Message | |
|---|---|
| 1 . | These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene ECHPCC20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| Sindustris PP H7512 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| NORYL™ PX2956 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Sylvin 7011EE-72 WHITE 1277 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4299-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |