Braskem PE FLEXUS7200XP
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mYoXMp_BraskemPEFLEXUS7200XP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem FLEXUS 7200XP is a Linear Low Density Polyethylene produced through metallocene catalyst. It was specially designed to provide outstanding processing performance. Films obtained with this grade show excellent mechanical and optical properties. It contains antioxidant additives. Applications Stretch films Process Recommended processing conditions for film extrusion about 220 - 270 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 180 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 990 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 250 | g | ASTM D1922 |
| TD : 25 µm, blown film | 460 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 1(60 °, 23.0 µm, blown film) | 149 | ASTM D2457 | |
| Transmittance 2(23.0 µm, blown film) | 93.8 | % | ASTM D1003 |
| Haze 3(23.0 µm) | 1.8 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cling 4(23.0 µm) | 16 | g | ASTM D4649 |
| Puncture 5(23.0 µm) | 3200 | g | ASTM D4649 |
| Retention Ending Force 6(23.0 µm) | 2500 | g | ASTM D4649 |
| Retention Loss 7(23.0 µm) | 30 | % | ASTM D4649 |
| Retention Maximum Force 8(23.0 µm) | 4100 | g | ASTM D4649 |
| Ultimate Test 9(23.0 µm) | 380 | % | ASTM D4649 |
| Note Message | |
|---|---|
| 1 . | 75%Flexus7200XP + 25% LLDPE Octene |
| 2 . | 75%Flexus7200XP + 25% LLDPE Octene |
| 3 . | 75%Flexus7200XP + 25% LLDPE Octene |
| 4 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| 5 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| 6 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| 7 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| 8 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| 9 . | 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPC 8 FR | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | PC | RC Plastics |
| RheTech Polypropylene CC40P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Novodur® Ultra 4115 | Styrolution | PC+ABS | Novodur® Ultra |
| Gallonprene® GP520-5012 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| PHOENIX™ 8652 | Phon Tech Industrial Company | TPE | PHOENIX™ |