Order Products : sales@su-jiao.com
BIOPLAST® 105
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | BIOTEC GmbH & Co. KG |
| Trademark: | BIOPLAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aPSHPc_BIOPLAST-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BIOPLAST 105 is BIOTEC's trademark for a completely new, plasticizer-free thermoplastic material. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST 105. The material is extremely suitable for injection moulding, sheet film extrusion and blown film extrusion of completely biodegradable products. The complete biodegradability and other functional properties enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 to 1.30 | g/cm³ | ISO 1183/A |
| Apparent Density | 0.75 to 0.83 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 to 11 | g/10 min | ISO 1133 |
| Particle Size | 3.00 to 4.00 | mm | |
| Water Content | < 0.50 | % | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | > 10 | µm | |
| Tensile Strength | ISO 527-3 | ||
| MD : 23°C, 10 µm | 20.0 to 50.0 | MPa | |
| TD : 23°C, 10 µm | 20.0 to 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 10 µm | 100 to 900 | % | |
| TD : Break, 10 µm | 100 to 900 | % | |
| Water Vapor Transmission Rate (10 µm) | 70 to 90 | g/m²/24 hr | DIN 53122 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.00 to 1.20 | g/cm³ | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5420F B2 | Spartech Polycom | PP, Unspecified | Spartech |
| COSMOPLENE® FL6416 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP, Unspecified | COSMOPLENE® |
| Ghaed ABS ABS-70SR | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
| OLEFISTA™ QX0238D | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| Plexiglas® Resist zk6BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |