Lumid®SG2460B is a polyamide 66 (nylon 66) material, which contains a 46% glass fiber reinforced material. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lumid®The main characteristics of the SG2460B are: beautiful. Lumid®The typical application fields of SG2460B are: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 196 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 11800 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 275 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 210 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 4.00 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 285 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 295 | °C | |
| Processing (Melt) Temp | 270 - 295 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.09% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 HF TFE 20 | RTP Company | PEEK | RTP |
| Sicoklar E01.19 | Ravago Group | PC | Sicoklar |
| Adell Polyamide AW-37 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Kpren 135C | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| INEOS PP 540-CA13 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |