| POLYAMIDE 66 FILLED WITH PTFE TO IMPROVE WEAR RESISTANCE MOULDED PARTS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 2.0 | % | ASTM D955 |
| -- | 2.0 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 8.5 | % | ASTM D570 |
| Saturated, 23°C | 8.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.8 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 70.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2500 | MPa | ASTM D790 |
| -- | 2350 | MPa | ISO 178 |
| Flexural Strength | 110 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 65 | J/m | ASTM D256 |
| 23°C | 65 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5085 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinpolene TPP1030 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Spartech Polycom PP5940 S35 | Spartech Polycom | PP Homopolymer | Spartech |
| EZPrene 9050D | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Hostacom TRC 411N W91470 | LyondellBasell Industries | PP Copolymer | Hostacom |