| Daplen ED306UBB is a 30% mineral filled polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 21.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2450 | MPa | ISO 178 |
| Flexural Stress | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 56.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 2002 | Kuraray Co., Ltd. | SEPS | SEPTON™ |
| ULTEM™ HU1110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Clariant Nylon 6/6 6604G33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Durolon® IR2500 | Unigel Plásticos | PC | Durolon® |
| HiFill® POM HO IM3 HF | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |