TOPAS® 9903D-10 Datasheet,COC,Topas Advanced Polymers, Inc.-SHANGHAI SUSHENG

TOPAS® 9903D-10

Category:	COC , Cyclic Olefin Copolymer
Manufacturer:	Topas Advanced Polymers, Inc.
Trademark:	TOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lwKOAw_TOPAS-9903D-10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Product Description TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended. Selected Applications Shrink films and labels Food packaging Food contact Leading Attributes High shrink at low temperatures, low stress, toughness Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 9506F-500 - robust low temperature (T g =65°C) extrusion grade TOPAS 9506F-04 - high clarity extrusion grade

Message

Product Description
TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended.

Selected Applications

Shrink films and labels

Food packaging

Food contact

Leading Attributes

High shrink at low temperatures, low stress, toughness

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

TOPAS 9506F-500 - robust low temperature (T g =65°C) extrusion grade

TOPAS 9506F-04 - high clarity extrusion grade

General Information
Features	High purity Moisture proof Rigidity, high Copolymer Good chemical resistance Good toughness Compliance of Food Exposure High shrinkage General BPA-free amorphous Halogen-free Medium transparency
Uses	Packaging Films Label Multilayer film Mixing cast film Food packaging General
Agency Ratings	FDA FCN 405 Europe 10/1/2011 12:00:00 AM
Forms	Particle
Processing Method	Film extrusion Blow film cast film Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.02	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	0.90	g/10 min	ISO 1133
230°C/2.16 kg	3.7	g/10 min	ISO 1133
260°C/2.16 kg	7.4	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR)			ISO 1133
190°C/2.16 kg	1.00	cm³/10min	ISO 1133
230°C/2.16 kg	4.00	cm³/10min	ISO 1133
260°C/2.16 kg	8.00	cm³/10min	ISO 1133
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	100	µm
Tensile Modulus (100 µm, cast film)	1260	MPa	ISO 527-3/1
Tensile Stress			ISO 527-3/50
MD : Fracture, 100 µm, cast film	25.0	MPa	ISO 527-3/50
TD : Fracture, 100 µm, cast film	22.0	MPa	ISO 527-3/50
Tensile Elongation			ISO 527-3/50
MD : Fracture, 100 µm, cast film	> 150	%	ISO 527-3/50
TD : Fracture, 100 µm, cast film	> 100	%	ISO 527-3/50
Oxygen Permeability (23°C, 100 µm, extruded film, 50% RH)	39	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (100 µm, 23°C, Cast Film, 85% RH)	0.19	g·mm/m²/atm/24 hr	ASTM F1249

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	33.0	°C	ISO 11357-2

Optical	Nominal Value	Unit	Test Method
Gloss (60 °, 100 µm, cast film)	> 100		ISO 2813
Haze (100 µm, cast film)	< 1.0	%	ISO 14782

Extrusion	Nominal Value	Unit
Feed part of extruder	20 - 60	°C
Extruder Screw L/D Ratio	> 28:1
Cylinder Zone 1 Temp.	210 - 220	°C
Cylinder Zone 2 Temp.	230 - 240	°C
Cylinder Zone 3 Temp.	230 - 240	°C
Cylinder Zone 4 Temp.	230 - 240	°C
Die Temperature	230 - 240	°C

Extrusion instructions
Head Pressure: P >140 bar / 2000 psi; Fine screen packs as neededScrew Speed: RPM > 50% nominalScrew Design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch

Resin Grade	Manufacturer	Category	Trademark
STERLENE™ BMU148A	R&P (Pte.) Ltd.	TPO (POE)	STERLENE™
ASI POLYPROPYLENE PP 2407-01	A. Schulman Inc.	PP Impact Copolymer	ASI POLYPROPYLENE
Flexalloy® 9400-80	Teknor Apex Company	PVC Elastomer	Flexalloy®
INSTRUC PPGF15FC	Infinity LTL Engineered Compounds	PP, Unspecified	INSTRUC
LNP™ VERTON™ MV00ASU compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ VERTON™

Resin Grade

Manufacturer