LNP™ STAT-KON™ OX00428 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lgmA3n_LNP-STAT-KON-OX00428-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON OX00428 is a compound based on PPS - Linear resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-O-00428 Product reorder name: OX00428 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 64.0 | MPa | ASTM D638 |
| Break | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3530 | MPa | ASTM D790 |
| -- 5 | 3270 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 111 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 116 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 49 | J/m | ASTM D256 |
| 23°C 7 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 8 | 16 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 2.28 | J | ASTM D3763 |
| -- | 0.520 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 153 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 159 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 112 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 5.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rulon® AR | Saint Gobain Performance Plastics | PTFE | Rulon® |
| BJB Polyurethane WC-783 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Dryflex® A1 600701 | ELASTO | SEBS | Dryflex® |
| Karina IVORY PVC COMPOUND 105900-35/1-B-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301/CF/15/TF/5 BK VP | Lehmann & Voss & Co. | PPS | LUVOCOM® |