Hifax CA 387 A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1EdVHf_Hifax-CA-387-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax CA 387 A is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell' s proprietary Catalloy process technology. It has high melt flow and an excellent balance of impact, stiffness, processability and paintability. Hifax CA 387 A is primarily used for painted automotive bumper fascias that require high durability, and for other injection molded parts with paintable and weatherable requirements. It is also utilized as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA387 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.5 | % | |
| Break | 75 | % | |
| Flexural Modulus - Chord 1(23°C) | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C, Complete Break | 7.0 | kJ/m² | |
| 23°C, Partial Break | 47 | kJ/m² | |
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -40°C, 3.20 mm, Energy at Peak Load, Ductile Failure | 27.0 | J | |
| 23°C, 3.20 mm, Energy at Peak Load, Ductile Failure | 17.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 74.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 47.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7HAA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Titacon® TX910 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Hanwha Total PP HJ730L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Hanwha Total PE E090A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| Jiangsu Sinarise PX851X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |