Evolue™-H SP6505
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | Evolue™-H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | leoEw5_Evolue--H-SP6505.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Evolue™-H SP6505 is a High Density Polyethylene product. It can be processed by blow molding and is available in Asia Pacific, Europe, or North America. Typical application: Containers. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.957 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.45 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | > 600 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 17 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746A, ISO 974 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 133 | °C | ISO 11357-3, ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9659-55 Yellow 4166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Badamid® B70 SM-Z3 | Bada AG | Nylon 6 | Badamid® |
| Clariant ABS ABS5475 | Clariant Corporation | ABS | Clariant ABS |
| Fortron® MT9141L4 DW | Celanese Corporation | PPS | Fortron® |
| Innothane® FM-109 | Innovative Polymers, Inc. | TSU | Innothane® |