Lucene™ SP 988
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lTq9Mk_Lucene-SP-988.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Description: SP 988, LG PE-RT Type II is a high performance PE for hot and cold water pipe. It was developed by using a new LG catalyst technology as well as new concept which lead to a BOCD(Broad Orthogonal Co-monomer Distribution) molecular structure. Pipes made out of SP 988 offer excellent properties to both processability and Long Term Hydrostatic Strength. SP988 conforms to the FDA regulation 21 CFR 177.1520. and the NSF/ANSI standard 61(drinking water system components-Health effects). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, F50) | > 10000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 20.6 | MPa | |
| Break | 36.3 | MPa | |
| Tensile Elongation 2(Break) | 750 | % | ASTM D638 |
| Flexural Modulus 3 | 579 | MPa | ASTM D790 |
| Internal Pressure Resistance | |||
| 1 Hr 4 | Pass | ||
| 1000 Hr 5 | Pass | ||
| 165 Hr 6 | Pass |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability - Hydrostatic Pressure Test 7 | Pass |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 20°C, 10 MPa |
| 5 . | 95°C, 3.5 Mpa |
| 6 . | 95°C, 3.6 Mpa |
| 7 . | 8760 Hr, 110°C, 1.9 Mpa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 50 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Supol HT315E | LyondellBasell Industries | PP Copolymer | Supol |
| Task® 11 | Smooth-On, Inc | PUR, Unspecified | Task® |
| INEOS PP L24G-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| Magnobond 6663-1 | Magnolia Plastics, Inc. | Epoxy | Magnobond |