Pibiflex® 6097 NERO900
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lCVVL2_Pibiflex-6097-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV stabilized TPC grade |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Flexural Modulus | 450 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 212 | °C | ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G30V0BLS | Kolon Plastics, Inc. | PBT | SPESIN® |
| Toraycon® 1100M | Toray Plastics (Malaysia) Sdn. Bhd. | PBT | Toraycon® |
| TOTAL Polystyrene 3241 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| NILENE® P K25T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| IPC PP 4810C-C | International Polymers Corporation | PP Copolymer | IPC PP |