Witcom PA6 2011/200
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kp3Yp2_Witcom-PA6-2011-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA6 2011/200 is a polyamide 6 (nylon 6) product that contains a filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 - 0.70 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 2.4 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.50 - 1.5 | % | ISO 527-2 |
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| Thermal Conductivity 1 | 1.6 | W/m/K | ASTM E1530 |
| RTI Imp (3.00 mm) | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Note Message | |
|---|---|
| 1 . | through plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8302-75C UV White 1486 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Topilene® J740 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| LNP™ STAT-KON™ OX92182 compound | SABIC Innovative Plastics Europe | PPS | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ CZL36 compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ LUBRICOMP™ |
| Monprene® MP-2951 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |