Moplen HP421H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kiGglA_Moplen-HP421H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP421H is a modified polypropylene homopolymer designed for the production of BOPP films at very high speed. BOPP films produced with HP421H feature good mechanical properties, excellent barrier against moisture, odours, oxygen, and good transparency and gloss. Coextruded films made of Moplen HP421H are widely used in the food packaging industry. Moplen HP421H is formulated with slip agent and antistatic. For regulatory information please refer to Moplen HP421H Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | ISO 527-2/50 |
| Fracture | 410 | % | ISO 527-2/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Additional Information |
|---|
| Typical Film Properties of monolayer film produced on T.M. Long equipment, a laboratory simultaneous film stretcher:-Tensile Tangent Modulus (0-1%), MA 18068, 5 mm/min, 20 µm: 2400 MPa-Stress at Break, MA 18068, 50 mm/min, 20 µm: 116 MPa-Elongation at Break, MA 18068, 50 mm/min, 20 µm: 29% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® LD2 PC 1000 14008 WT1009-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |
| Hanwha Total PP FB76S | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| ESTACARB 0820 GF | Cossa Polimeri S.r.l. | PC | ESTACARB |
| INEOS PP N02G-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| LUVOCOM® 80-8842 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |