Liquid Silicone Rubber (LSR) raw material for medical device and component fabrication in the Healthcare Industry APPLICATIONS Silastic® Q7-7840 Liquid Silicone Rubber, Silastic ® Q7-7850 Liquid Silicone Rubber, and Silastic ® Q7-7870 Liquid Silicone Rubber, Parts A and B, are heat-cured elastomers for use by customers fabricating medical devices, including those intended for implantation in humans for less than 30 days and non-implant applications. Silastic Q7-7840 Liquid Silicone Rubber, Silastic Q7-7850 Liquid Silicone Rubber, and Silastic Q7-7870 Liquid Silicone Rubber are two-part platinum-catalyzed silicone elastomers specifically designed for liquid injection molding or supported extrusion. The elastomer is supplied as a two-part kit (Part A and Part B), equal portions (by weight) of which must be thoroughly blended together prior to use. The elastomers are thermally cured via an addition-cure (platinum catalyzed) reaction. When blended and cured as indicated the resulting elastomers consist of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica. The elastomer can be used without any post-cure. Furthermore, the cured elastomer is heat stable up to 204°C (400°F), can be autoclaved, and exhibits high gas permeability compared with most other thermoset elastomers and thermoplastics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.3 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 48 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (200% Strain) | 2.60 | MPa | ASTM D412 |
| Tensile Strength | 9.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 660 | % | ASTM D412 |
| Tear Strength 1 | 48.2 | kN/m | ASTM D624 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Rate - MDR T90 2(150°C) | 29.0 | sec |
| Note Message | |
|---|---|
| 1 . | B mould |
| 2 . | 3 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LMP322 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Kazan HDPE PEBOB-7D1K | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| LNP™ KONDUIT™ OX11315 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |
| OxyVinyls庐 220F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| PIVINEL™ BC-33 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |