VESTAMID® L L2106F
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kIKs9Q_VESTAMID-L-L2106F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unfilled polyamid 12 compounds Characterization: high viscos, improved transparency, modified by comonomers Application Examples: flexible tubular films for sausage casings The properties of PA 12 compounds can be modified to suit the requirements of many applications by incorporating various additives such as stabilizers, plasticizers, reinforcements, and fillers. The VESTAMID® L compounds of Evonik comprise a range of various products that are customized to the requirements of processors and users. Many of the PA 12 compounds are suitable especially for the injection molding of recision parts; others have been developed specifically for the extrusion process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.8 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 7.0 | kJ/m² | |
| 23°C, Complete Break | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 40.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 170 | °C | ISO 306/A |
| -- | 130 | °C | ISO 306/B |
| Melting Temperature 1 | 175 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.70 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 0.045 | ||
| 23°C, 1 MHz | 0.028 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 600 | V | |
| Solution A 2 | > 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A1 | IEC 60426 |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| 2 . | 50 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G40P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| SAXAMID™ 236F6Q32 | SAX Polymers | Nylon 66 | SAXAMID™ |
| Tarnamid® T- 27 P | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Nucrel® 0903HC | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| EXTEM™ VH1003P resin | SABIC Innovative Plastics Europe | PEI | EXTEM™ |