Marvel™ M90
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | Marvel™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k9q9m8_Marvel-M90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M9001RW and Marvel M90 are linear-low density polyethylene (LLDPE) for rotational molding applications. M90 is a color compounded form. With excellent stiffness good impact strength and toughness.Both of them are suitable for rotational molding of large water tanks and other general rotational molded articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 21.0 | MPa | ASTM D638 |
| Fracture | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1100 | % | ASTM D638 |
| Flexural Modulus | 750 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact 3(-40°C) | 122 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Point | 113 | °C | ASTM D2117 |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Melting Temperature | 127 | °C | ASTM D2117 |
| Additional Information |
|---|
| UV Resistance Level: ASTM 2565: 8Typical Oven Temperature: 250 to 300°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5 mm rotomolded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIREX MP6500 | Formosa Plastics Corporation | PS (MIPS) | TAIRIREX |
| Celstran® PP-GF40-0414 P7/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Fainplast PVC GS 65/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lucent PP PPC-310 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| LEXAN™ LUX9136C resin | SABIC Innovative Plastics | PC | LEXAN™ |