Pro PP-HO-30T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Pro Polymers |
| Trademark: | Pro-Comp™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k7wEtl_Pro-PP-HO-30T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-HO-30T is a 30% Talc Filled, Polypropylene Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 1.0 | % | ASTM D955 |
| Transverse flow : 3.18mm | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.0 | MPa | ASTM D638 |
| Flexural Modulus | 2890 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Dart Drop Impact | 0.800 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 126 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 72.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 230°C/2.1kgf: 8 to 12 g/10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ F5134T2-4 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| POLYMAN® (ABS) LP 330 | A. Schulman Europe | ABS | POLYMAN® |
| Scolefin 53 H 10-81 | Ravago Group | PP Homopolymer | Scolefin |
| ADENE NCQAGD | A.D. Compound spa | PP Copolymer | ADENE |
| MTEGRITY™ LLDPE LL204AA | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |