Michilene F8100GCMN35
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michilene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k2A4GW_Michilene-F8100GCMN35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Michilene F8100GCMN35 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 35% glass\mineral. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 5720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 143 | °C | |
| 1.8 MPa, Unannealed | 127 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 221 | °C | |
| Middle Temperature | 221 | °C | |
| Front Temperature | 224 | °C | |
| Nozzle Temperature | 227 | °C | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 37.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A1 GF 30 LW | A. Schulman Europe | PBT+PET | SCHULADUR® |
| Teslin® SP 1400 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| 4POM® 23I10000 | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| JSR EPR T7881F | JSR Corporation | EPDM | JSR EPR |
| LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |