Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 7 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 260 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/1A/5 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 260 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 280 - 285 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Nozzle Temperature | 310 - 320 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 120 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 300 to 315°CZone 4 Temperature: 300 to 310°CFeed Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ GTX985 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |
| BUP 626 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| ENFLEX EA3575A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| K-vinyl 20 A 90 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Sylvin 7868-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |