Borealis PP MS64T20
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ifyXLg_Borealis-PP-MS64T20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MS64T20 is a 20% mineral filled polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 93.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | 13 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 0.60 | kJ/m² | ISO 179/1eA |
| -20°C | 1.2 | kJ/m² | ISO 179/1eA |
| 23°C | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | ISO 179/1eU |
| 23°C | 38 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 2.1 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| CLTE - Flow (-30°C) | 5.6E-5 | cm/cm/°C | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hrs (100°C) | 5.0E-4 | g | DIN 75201 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS5000 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Tool-A-Thane UT-705 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Witcom PE 4L1 | Witcom Engineering Plastics B.V. | PE, Unspecified | Witcom PE |
| New-prene™ 6050N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| EVICOM™ GRS 5015 AD1 | INEOS Compounds | PVC, Flexible | EVICOM™ |