PLASTRON™ PA66-CF40-02
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | PLASTRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | idOyrZ_PLASTRON-PA66-CF40-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLASTRON™ PA66-CF40-02 is a Polyamide 66 (Nylon 66) material filled with 40% glass fiber. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield) | 330 | 290 | MPa | ISO 527-2 |
| Flexural Modulus | 28000 | 24000 | MPa | ISO 178 |
| Flexural Stress | 490 | 420 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | 26 | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 262 | -- | °C | ISO 75-2/A |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Moisture Content | -- | 0.90 | % |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8512N-02 | Colorite Polymers | PVC, Flexible | Unichem |
| APEX® 79-B427D-46 Black | Teknor Apex Company | PVC, Flexible | APEX® |
| Hostalen PP H2150 304850 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| Hifax TRC 228P 2 C12637 | LyondellBasell Industries | PP Copolymer | Hifax |
| 3M™ Dyneon™ Fluoroelastomer MIP 8640X | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |