LNP™ LUBRICOMP™ KL004U compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZCSiYx_LNPLUBRICOMPKL004Ucompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KL004U is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP Fulton* Tradename. Also known as: LNP* LUBRICOMP* Compound 404 UV Product reorder name: KL004U |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.0 - 2.5 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 2.5 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.0 - 2.5 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.0 - 2.5 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2140 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.1 | MPa | ASTM D638 |
| Yield | 47.3 | MPa | ISO 527-2 |
| Fracture | 50.9 | MPa | ASTM D638 |
| Fracture | 46.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 11 | % | ASTM D638 |
| Yield | 9.6 | % | ISO 527-2 |
| Fracture | 18 | % | ASTM D638 |
| Fracture | 23 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.6 | MPa | ASTM D790 |
| -- | 79.3 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.29 | ASTM D3702 Modified | |
| With Self-Static | 0.15 | ASTM D3702 Modified | |
| Wear Factor - Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 3 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.40 | J | ASTM D3763 |
| -- | 0.770 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 157 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 99.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 98.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C30ST4 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| TAIRIPRO K7025 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Alpha PVC GW 3026 NAT.LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Fainplast PVC KL 87 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ESTOPLAST XU 245NN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |