| Unreinforced Polybutylene Terephthalate Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 1.7 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.50 | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2600 | MPa | ISO 899-1 |
| 1000 hr | 1800 | MPa | ISO 899-1 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 130 | kJ/m² | ISO 180/1U |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 60.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 55.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 175 | °C | ISO 306/B50 |
| Melting Temperature 2 | 223 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.11 | g/cm³ | |
| Specific Heat Capacity of Melt | 2100 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.21 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 S-65D | RTP Company | TPU-Polyester | RTP |
| Sylvin 8842A Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Taitacell EPS 351FA | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| NYLOY® UB-0010N C40N2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| THERMOLAST® K TF4ADN (Series: FC/AD1/PS) | KRAIBURG TPE | TPE | THERMOLAST® K |