POLYasa 2008F
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYasa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hupGH9_POLYasa-2008F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV-stabilized High flow |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 8940 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LAPEROS® T130 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| Jackdaw PC DR15NT6341 | Jackdaw Polymers | PC | Jackdaw PC |
| LNP™ LUBRICOMP™ RP004SZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| PENTALLOY BS 6 GV10 H schwarz | PENTAC Polymer GmbH | ABS+Nylon | PENTALLOY BS |