RheTech Polypropylene G20P252-01A
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y0mAUr_RheTech-Polypropylene-G20P252-01A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Fiber Reinforced, Polypropylene Copolymer, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.7 | MPa | ASTM D638 |
| Flexural Modulus | 3520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Dart Drop Impact | 0.678 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 199 - 227 | °C | |
| Middle Temperature | 204 - 232 | °C | |
| Front Temperature | 210 - 238 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - application dependentScrew RPM: Recovery 3 seconds before mold opensCycle Time: Variable - wall thickness dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB2000-8 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Mecoline S RDX 1247 F | Melos GmbH | TP, Unspecified | Mecoline |
| TECHNYL® 1021GF6 BLACK 0179 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Vyncolit® X658 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Hylon® N2000STL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |