HOPELEN SJ-170T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hCpgBZ_HOPELEN-SJ-170T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SJ-170T is homo polymer resin produced through the polymerization of propylene. This grade is designed to be processed in conventional Injection molding equipment. SJ-170T shows good thermal stability and high melt-flow. It is typically used in production of housewares, the transparency stationery and disposable syringes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 37.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | < 100 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C | 20 | J/m | |
| 23°C | 25 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ GTX964 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |
| NuSil CV2-1142 | NuSil Technology | Silicone | NuSil |
| Colorite CS Series CS9040UL-85B | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Ebalta LH 25 / Resin+Hardener | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Karina COMP. PVC GRAY -E 751D18/676-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |