RANPELEN SFO-130A
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | RANPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h7ggEN_RANPELEN-SFO-130A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HOPELEN SFO-130A is homo polymer resin produced by the polymerization of propylene. This grade is designed to be processed in metallizing BOPP film applications. This grade shows good gloss and transparence properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | < 1.0 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 150 | °C | ASTM D1525 |
| Melting Temperature | 165 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm, Blown Film) | < 0.90 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1770 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 280.5H | RTP Company | Nylon 66 | RTP |
| TES J-4/30 BK | Techmer Engineered Solutions | Nylon 612 | TES |
| Capran Medallion® 1500 film | Honeywell | Nylon 6 | Capran Medallion® |
| Karina IVORY PVC COMPOUND 105471-35/1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |