Glastic® UTS 1478
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Glastic Corporation |
| Trademark: | Glastic® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gzVIcq_Glastic-UTS-1478.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glastic UTS 1478 is a fiberglass-reinforced laminate. This resin is ideal for applications requiring flame and heat resistance, as well as applications requiring higher retention of properties after heat aging. Glastic UTS 1478 is ideal for a wide variety of applications, including intricate punchings for switches, switch plates, controls, control panels, and terminal boards. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (yield, 1.60mm) | 61.4 | MPa | ASTM D638 |
| Flexural Strength (yield, 1.60mm) | 170 | MPa | ASTM D790 |
| Compressive Strength (1.60 mm) | 269 | MPa | ASTM D695 |
| Shear Strength | 92.4 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (1.60 mm) | 570 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (1.60 mm) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.26 | W/m/K | ASTM C177 |
| RTI Elec (1.60 mm) | 130 | °C | UL 746 |
| RTI (1.60 mm) | 160 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| 1.60 mm, in Air | 17 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 22 | kV/mm | ASTM D149 |
| Dissipation Factor | ASTM D150 | ||
| 1.60 mm, 60 Hz | 0.011 | ASTM D150 | |
| 1.60 mm, 1 MHz | 0.010 | ASTM D150 | |
| Arc Resistance (1.60 mm) | 130 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (1.60 mm) | 500 | V | UL 746 |
| High Amp Arc Ignition (HAI) (1.60 mm) | 200 | UL 746 | |
| Hot-wire Ignition (HWI) (1.60 mm) | 300 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Oxygen Index (1.60 mm) | 36 | % | ASTM D2863 |
| Additional Information |
|---|
| NEMA Grade: GPO-2/GPO-2PMilitary Specification: L-P 509/GPO-2Insulation Resistance, ASTM D257: 2.7e10 ohmsIgnition Time: 81 minBurn Time: 48 min |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN 3O 51 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| NEXT REGRIND PC LS1-100RG | NEXT Specialty Resins, Inc. | PC | NEXT REGRIND |
| TECHNYL® A 218C V10 NATURAL S | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Kanghui KH2120 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |
| LEXAN™ SLX2471T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |