TOTAL Polystyrene Impact 3630
| Category: | PS (MIPS) , Medium Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gc8Hh7_TOTAL-Polystyrene-Impact-3630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYSTYRENE IMPACT 3630 is an easy flowing, medium impact polystyrene for injection moulding. This grade offers a good compromise of flow and softening point allowing for the production of large and complex articles at good cycle times. The ease of colouration and good surface finish of this grade give a wide range of applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.04 | g/cm³ | ISO 1183 |
| -- | 1040 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Melt volume-flow rate (200°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | < 0.10 | % | ISO 62 |
| Saturation | 0.10 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 32.0 | MPa | ISO 527-2 |
| Break | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 1.5 | % | ISO 527-2 4 |
| Break | 30 | % | ISO 527-2 |
| Nominal strain at break | 30 | % | ISO 527-2 5 |
| Tensile Creep Modulus (1 hr) | 2400 | MPa | ISO 899-1 6 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.00 | kJ/m² | ISO 179/1eA 7 |
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 77.0 | °C | ISO 75-2/A |
| 1.8 MPa | 78.5 | °C | ISO 75-2 8 |
| Vicat Softening Temperature | |||
| -- | 89.0 | °C | ISO 306/A50 |
| -- | 82.0 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 81.0 | °C | ISO 306 9 |
| CLTE | |||
| Flow | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 9.0E-5 | cm/cm/°C | ISO 11359-2 10 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | > 1.0E+14 | ohms | IEC 60093 |
| -- | 1.0E+13 | ohms | IEC 60093 11 |
| Electric Strength | 150 | kV/mm | IEC 60243-1 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 HF NTLA010 NR430 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Devcon Wear Guard™ Ultra | Devcon | Epoxy | Devcon |
| Panlite® L-1225LM | TEIJIN LIMITED | PC | Panlite® |
| Sylvin 3240-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRILOY™ D2000I compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |