Abstron IMC-45M
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWVsRl_Abstron-IMC-45M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS-polycarbonate alloys for High service temperature appplications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Flexural Modulus (6.40 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.20 mm | 590 | J/m | ASTM D256 |
| 6.40 mm | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 230 - 290 | °C | |
| Mold Temperature | 105 - 115 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Drying Time (Tray Oven): 5 to 7 hrDrying Time (Hopper Dryers): 4 to 5 hrDrying Time (Dry Air Ovens): 3 to 4 hrInjection Pressure: Medium to HighBack Pressure: Medium to High |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PBT 3055G30 (FR) | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| NEXT SIGNATURE PPH G30-300 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |
| Akulon® K224-PG8 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| EPO-TEK® OG142-112 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| ICORENE® 9105 V0 Grey 7005 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |