LNP™ THERMOCOMP™ JF004EXP compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFM86W_LNPTHERMOCOMPJF004EXPcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004EXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound JF-1004 EM Product reorder name: JF004EXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7360 | MPa | ASTM D638 |
| -- | 7590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 114 | MPa | ASTM D638 |
| Fracture | 109 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 6690 | MPa | ASTM D790 |
| -- | 7590 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 186 | MPa | ASTM D790 |
| -- | 183 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 73 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.0 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 206 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 205 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 371 - 382 | °C | |
| Processing (Melt) Temp | 354 - 371 | °C | |
| Mold Temperature | 138 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TE250F9 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Wellamid® XT1627-BK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Altuglas® BS 684 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| HAIPLEN H90 T4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| SQUARE® SCR2524-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |