MAJORIS DG504X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFD73G_MAJORIS-DG504X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS DG504X is a high performance reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. MAJORIS DG504X has been developed especially for demanding applications in various engineering sectors. MAJORIS DG504X has high rigidity and impact strength, good dimensional stability, very good stiffness and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.59 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 115 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 11400 | MPa | ISO 178 |
| Flexural Stress | 174 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 164 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Screw speed: Low to mediumBack pressure: Low to medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP512-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Chiao Fu PA6 MC212G40 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| Hyundai EP XLPE XP680/Natural | HYUNDAI EP Co., Ltd. | XLPE | Hyundai EP XLPE |
| LEXAN™ LUX2414G resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina BLUE PVC COMPOUND 701D06/ 8-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |