Sarlink® TPV X6165N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CVRg6X_Sarlink-TPV-X6165N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® X6165N is an engineered material designed primarily for demanding consumer, building & construction, and automotive interior applications. Available only in natural. Sarlink® X6165N exhibits excellent compression set and flex fatigue, high and low temperature performance. The material can be processed by injection molding, blow molding and extrusion for applications such as building profiles, interior car applications, colored compounds and tube, boots and bellows. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.943 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A, 5 seconds, extruded | 62 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 62 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain | 2.00 | MPa | ISO 37 |
| Flow : 100% strain | 2.80 | MPa | ISO 37 |
| Tensile Stress | ISO 37 | ||
| Acos flow : Yield | 5.60 | MPa | ISO 37 |
| Flow : Yield | 4.50 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : Fracture | 690 | % | ISO 37 |
| Flow : Fracture | 400 | % | ISO 37 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 31 | % | ISO 815 |
| 70°C, 22 hr | 37 | % | ISO 815 |
| 100°C, 22 hr | 41 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 215 | °C | |
| Middle Temperature | 180 - 215 | °C | |
| Front Temperature | 180 - 215 | °C | |
| Nozzle Temperature | 187 - 220 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 205 | °C | |
| Cylinder Zone 3 Temp. | 187 - 210 | °C | |
| Cylinder Zone 4 Temp. | 187 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C | |
| Die Temperature | 195 - 215 | °C | |
| Take-Off Roll | 20.0 - 50.0 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: 3:1 Compression Ratio |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reblend® B4070 NATURALE | SO.F.TER. SPA | PC+ABS | Reblend® |
| Chiao Fu PA66 MD312LA10 | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| ESTAPROP KUR 4000 CH/TD | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Karina IVORY PVC COMPOUND 837-35/1-E-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETILEN I10-19T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |